CHX Stabilizes the Resin/demineralized Dentin Interface.

The aim of this study was to evaluate the effect of 2% chlorhexidine digluconate (CHX) on microtensile bond strength (µTBS) between an adhesive system and under 3 dentin conditions. For that, this study evaluated the adhesive interface at initial, after 6 months and 1 year of storage. Forty-eight human third molars were prepared and randomly divided into 3 groups, according to dentin substrates: sound dentin (Sd), caries-infected dentin (Ci) and caries-affected dentin (Ca). The groups were subdivided into two according to the dentin pre-treatment: application of 2% CHX or without pre-treatment (control). The dentin surfaces were etched with 35% phosphoric acid gel and bonded with Adper Single Bond 2 (3M ESPE) adhesive system according to manufacturer's instructions. Subsequently, the specimens were stored in deionized water at 37°C for 24h, 6 months and 1 year. Two additional teeth were used to analyze the bonding interfaces by SEM. Data was submitted to three-way ANOVA in a split plot design and Tukey's test (α = 0.05). The results showed that Ci decreased µTBS values when compared to Ca and Sd, regardless storages time or treatment. Stored samples for 6 months and 1 year decreased the µTBS for the control group, but no difference was found between storages time for the CHX group. As a conclusion, the 2% CHX application after etching showed improved dentin bond strength in the storage time, regardless of the substrates evaluated.

Partial anterior indirect restorations in cases with dentin exposure.

The partial anterior ceramic restoration is a predictable and durable treatment modality that reestablishes not only esthetics but also strength and function. Bio-emulation, minimally invasive dentistry, and adhesive technology are key to a successful restoration. Partial restorations are only indicated when teeth have enough hard tissue on which to bond veneers. When there is more than 50% of dentin exposure, many clinicians still rely on macromechanical retention by performing a full-crown preparation. However, new research has shown good survival rates for partial restorations with extensive dentin exposure. The present article describes two cases in which a step-by-step protocol was applied to bond a laminate veneer to a tooth with dentin exposure.

CHX stabilizes the resin/demineralized dentin interface

Abstract The aim of this study was to evaluate the effect of 2% chlorhexidine digluconate (CHX) on microtensile bond strength (µTBS) between an adhesive system and under 3 dentin conditions. For that, this study evaluated the adhesive interface at initial, after 6 months and 1 year of storage. Forty-eight human third molars were prepared and randomly divided into 3 groups, according to dentin substrates: sound dentin (Sd), caries-infected dentin (Ci) and caries-affected dentin (Ca). The groups were subdivided into two according to the dentin pre-treatment: application of 2% CHX or without pre-treatment (control). The dentin surfaces were etched with 35% phosphoric acid gel and bonded with Adper Single Bond 2 (3M ESPE) adhesive system according to manufacturer's instructions. Subsequently, the specimens were stored in deionized water at 37°C for 24h, 6 months and 1 year. Two additional teeth were used to analyze the bonding interfaces by SEM. Data was submitted to three-way ANOVA in a split plot design and Tukey's test (α = 0.05). The results showed that Ci decreased µTBS values when compared to Ca and Sd, regardless storages time or treatment. Stored samples for 6 months and 1 year decreased the µTBS for the control group, but no difference was found between storages time for the CHX group. As a conclusion, the 2% CHX application after etching showed improved dentin bond strength in the storage time, regardless of the substrates evaluated.

Resumo O objetivo deste estudo foi avaliar o efeito do digluconato de clorexidina 2% (CHX) na resistência de união à microtração (µTBS) entre um sistema adesivo e sob 3 condições de dentina. Para tanto, este estudo avaliou a interface adesiva no início, após 6 meses e 1 ano de armazenamento. Quarenta e oito terceiros molares humanos foram preparados e divididos aleatoriamente em 3 grupos, de acordo com os substratos dentinários: dentina hígida (Dh), dentina infectada por cárie (Di) e dentina afetada por cárie (Da). Os grupos foram subdivididos em dois de acordo com o pré-tratamento: aplicação de CHX 2% ou sem pré-tratamento (controle). As superfícies da dentina foram condicionadas com gel de ácido fosfórico a 35%, em seguida, utilizou-se o sistema adesivo Adper Single Bond 2 (3M ESPE) de acordo com as instruções do fabricante. Posteriormente, os corpos-de-prova foram armazenados em água deionizada a 37°C por 24h, 6 meses e 1 ano. Dois dentes adicionais foram usados ​​para analisar as interfaces de união no MEV. Os dados foram submetidos a ANOVA três fatores em esquema de parcela subdividida e ao teste de Tukey (α = 0,05). Os resultados mostram que a Di diminuiu os valores de µTBS quando comparado as Da e Dh, independente do tempo de armazenamento ou tratamento. Amostras armazenadas por 6 meses e 1 ano diminuíram a µTBS para o grupo de controle, mas nenhuma diferença foi encontrada entre o tempo de armazenamento para o grupo CHX. A aplicação de CHX 2% após o condicionamento apresentou melhora na resistência de união à dentina no tempo de armazenamento, independente dos substratos avaliados.

Seeing is believing? When scanning electron microscopy (SEM) meets clinical dentistry: The replica technique.

In restorative dentistry, the in situ replication of intra-oral situations, is based on a non-invasive and non-destructive scanning electron microscopy (SEM) evaluation method. The technique is suitable for investigation restorative materials and dental hard- and soft-tissues, and its interfaces. Surface characteristics, integrity of interfaces (margins), or fracture analysis (chipping, cracks, etc.) with reliable resolution and under high magnification (from ×50 to ×5,000). Overall the current study aims to share detailed and reproducible information about the replica technique. Specific goals are: (a) to describe detailed each step involved in producing a replica of an intra-oral situation, (b) to validate an integrated workflow based on a rational sequence from visual examination, to macrophotography and SEM analysis using the replica technique; (c) to present three clinical cases documented using the technique. A compilation of three clinical situations/cases were analyzed here by means the replica technique showing a wide range of possibilities that can be reached and explored with the described technique. This guidance document will contribute to a more accurate use of the replica technique and help researchers and clinicians to understand and identify issues related to restorative procedures under high magnification.

Effects of surface treatments on mechanical behavior of sintered and pre-sintered yttria-stabilized zirconia and reliability of crowns and abutments processed by CAD/CAM.

PURPOSE: This study evaluates the micro shear bond strength of resin cement to an yttriastabilized zirconia ceramic and the survival probability of zirconia abutments and crowns after different surface treatments through a fatigue test. MATERIALS AND METHODS: The study was divided into two parts. For part 1, 95 zirconia disks were divided into five groups (n = 19): control, untreated, airborne particle abrasion with Al2O3 particles before sintering, airborne particle abrasion with Al2O3 particles after sintering, silicatization before sintering, and silicatization after sintering. Three samples of each group were used for evaluation of surface roughness by confocal laser scanning microscopy and afterward were prepared for surface microstructural analysis by scanning electron microscopy. Ten samples of each group were subjected to micro shear bond strength testing, and the interfaces of the remaining six were examined by scanning electron microscopy. In part 2, 70 external hex zirconia abutments and copings were made by computer-aided design/computer-aided manufacturing (n = 14). Marginal fit of abutment/coping was measured in a confocal laser scanning microscope. Afterward, a fatigue test was carried out with progressive load of 80 up to 320 N (40 N steps), 5 Hz frequency, and 20,000 cycles at each step. Thermal cycling was simultaneously performed (5°C to 55°C). RESULTS: The group treated after sintering with SiO achieved statistically higher micro shear bond strength (P < .01). Higher failure loads were associated with a combined failure. The surface changes in the group treated with SiO before sintering suggest silica deposition, and there was a lack of homogeneity, which was more evident on the surface of the groups treated before sintering. The marginal gap was higher for the group treated before sintering with SiO (P < .01), and the survival probability of the sets was similar for all tested groups (P = .57). CONCLUSION: The micro shear bond strength to zirconia was improved after silicatization after sintering, but the survival probability of crown/abutment/implant sets was not affected by different surface treatments.

Influence of Different Dentin Substrate (Caries-Affected, Caries-Infected, Sound) on Long-Term µTBS.

The aim of this study was to evaluate the µTBS in different dentin substrates and water-storage periods. Twenty-four dentin blocks obtained from sound third molars were randomly divided into 3 groups: Sound dentin (Sd), Caries-affected dentin (Ca) and Caries-infected dentin (Ci). Dentin blocks from Ca and Ci groups were subjected to artificial caries development (S. mutans biofilm). The softest carious tissue was removed using spherical drills under visual inspection with Caries Detector solution (Ca group). It was considered as Ci (softer and deeply red stained dentin) and Ca (harder and slightly red stained dentin). The Adper Single Bond 2 adhesive system was applied and Z350 composite blocks were built in all groups. Teeth were stored in deionized water for 24 h at 37 ºC and sectioned into beams (1.0 mm2 section area). The beams from each tooth were randomly divided into three storages periods: 24 h, 6 months or 1 year. Specimens were submitted to µTBS using EZ test machine at a crosshead speed of 1.0 mm/min. Failure mode was examined by SEM. Data from µTBS were submitted to split plot two-way ANOVA and Tukey's HSD tests (a=0.05). The µTBS (MPa) of Sd (41.2) was significantly higher than Ca (32.4) and Ci (27.2), regardless of storage. Ca and Ci after 6 months and 1 year, presented similar µTBS. Mixed and adhesive failures predominated in all groups. The highest µTBS values (48.1±9.1) were found for Sd at 24 h storage. Storage of specimens decreased the µTBS values for all conditions.

Influence of Different Dentin Substrate (Caries-Affected, Caries-Infected, Sound) on Long-Term muTBS

Abstract The aim of this study was to evaluate the μTBS in different dentin substrates and water-storage periods. Twenty-four dentin blocks obtained from sound third molars were randomly divided into 3 groups: Sound dentin (Sd), Caries-affected dentin (Ca) and Caries-infected dentin (Ci). Dentin blocks from Ca and Ci groups were subjected to artificial caries development (S. mutans biofilm). The softest carious tissue was removed using spherical drills under visual inspection with Caries Detector solution (Ca group). It was considered as Ci (softer and deeply red stained dentin) and Ca (harder and slightly red stained dentin). The Adper Single Bond 2 adhesive system was applied and Z350 composite blocks were built in all groups. Teeth were stored in deionized water for 24 h at 37 ºC and sectioned into beams (1.0 mm2 section area). The beams from each tooth were randomly divided into three storages periods: 24 h, 6 months or 1 year. Specimens were submitted to µTBS using EZ test machine at a crosshead speed of 1.0 mm/min. Failure mode was examined by SEM. Data from µTBS were submitted to split plot two-way ANOVA and Tukey’s HSD tests (a=0.05). The µTBS (MPa) of Sd (41.2) was significantly higher than Ca (32.4) and Ci (27.2), regardless of storage. Ca and Ci after 6 months and 1 year, presented similar µTBS. Mixed and adhesive failures predominated in all groups. The highest µTBS values (48.1±9.1) were found for Sd at 24 h storage. Storage of specimens decreased the µTBS values for all conditions.

Resumo O objetivo neste estudo foi avaliar a resistência de união à microtração (RUµT) de um sistema adesivo convencional (Adper Single Bond 2 - SB) em diferentes substratos dentinários e períodos de armazenagem. Vinte e quatro blocos de dentina foram obtidos de terceiros molares hígidos e separados aleatoriamente em 3 grupos (n=8): dentina sadia (Ds), dentina afetada (Da) e dentina infectada (Di). A Da e a Di foram submetidas ao desenvolvimento biológico artificial de cárie (S. mutans). O tecido cariado amolecido foi removido usando broca esférica sob inspeção visual com a solução Caries Detector (grupo Da). Considerou-se como Di a dentina amolecida e fortemente pigmentada de vermelho e como Da, a dentina hígida e levemente pigmentada de vermelho. O sistema adesivo SB foi aplicado de acordo com as recomendações do fabricante e blocos da resina composta Z350 foram construídos (6 mm de altura). O conjunto (dente/bloco de resina) foi armazenado em água deionizada por 24 horas a 37 °C. Estes foram seccionados em palitos (1,0 mm2 de área), que foram separados aleatoriamente em 3 períodos de armazenagem: 24 horas, 6 meses e 1 ano. Os palitos foram submetidos ao ensaio de resistência de união à microtração na máquina EZ teste a uma velocidade de 1,0 mm/min. Dados de RUµT foram submetidos à Análise de Variância 2 fatores em esquema de parcela subdividida e ao teste de Tukey (a=0,05). Os valores de resistência (MPa) da Ds (41,2) foram significativamente maiores do que os da Da (32,4) e Di (27,2), independente do tempo de armazenagem. Di e Da, 6 meses e 1ano, apresentaram valores similares de resistência de união. As falhas adesivas e mistas foram predominantes para todos os grupos. Em conclusão, os maiores valores de RUµT (48,1±9,1) foram verificados para a Ds e 24 h de armazenagem. A armazenagem diminuiu os valores de RUµT para todas as condições.

Bacterial Adhesion and Surface Roughness for Different Clinical Techniques for Acrylic Polymethyl Methacrylate.

This study sought to assess the effect of different surface finishing and polishing protocols on the surface roughness and bacterial adhesion (S. sanguinis) to polymethyl methacrylates (PMMA). Fifty specimens were divided into 5 groups (n = 10) according to their fabrication method and surface finishing protocol: LP (3 : 1 ratio and laboratory polishing), NF (Nealon technique and finishing), NP (Nealon technique and manual polishing), MF (3 : 1 ratio and manual finishing), and MP (3 : 1 ratio and manual polishing). For each group, five specimens were submitted to bacterial adhesion tests and analyzed by scanning electron microscopy (SEM). Two additional specimens were subjected to surface topography analysis by SEM and the remaining three specimens were subjected to surface roughness measurements. Data were compared by one-way ANOVA. The mean bacterial counts were as follows: NF, 19.6 ± 3.05; MP, 5.36 ± 2.08; NP, 4.96 ± 1.93; MF, 7.36 ± 2.45; and LP, 1.56 ± 0.62 (CFU). The mean surface roughness values were as follows: NF, 3.23 ± 0.15; MP, 0.52 ± 0.05; NP, 0.60 ± 0.08; MF, 2.69 ± 0.12; and LP, 0.07 ± 0.02 (µm). A reduction in the surface roughness was observed to be directly related to a decrease in bacterial adhesion. It was verified that the laboratory processing of PMMA might decrease the surface roughness and consequently the adhesion of S. sanguinis to this material.

Influence of crosshead speed on failure load and failure mode of restored maxillary premolars.

We analyzed the effect of the crosshead speed of an applied load on failure load and failure mode of restored human premolars. Fifty intact, noncarious human premolars were selected. Class II mesio-occlusodistal preparations were made with a water-cooled high-speed preparation machine, and the teeth were restored with composite resin. The specimens were divided into five groups (n = 10 each) and tested individually in a mechanical testing machine, in which a 6.0-mm-diameter steel cylinder was mounted to vary the crosshead speed: v0.5: 0.5 mm/min; v1: 1.0 mm/min; v2.5: 2.5 mm/min; v5: 5.0 mm/min; and v10: 10.0 mm/min. The cylinder contacted the facial and lingual ridges beyond the margins of the restorations. Peak load to fracture was measured for each specimen (N). The means were calculated and analyzed with one-way analysis of variance followed by Tukey's test (a = 0.05). The mean load at failure values were (N) as follows: v0.5, 769.4 ± 174.8; v1, 645.2 ± 115.7; v5, 614.3 ± 126.0; v2.5, 609.2 ± 208.1; and v10, 432.5 ± 136.9. The fracture modes were recorded on the basis of the degree of the tooth structural and restorative damage: (I) fracture of the restoration involving a small portion of the tooth; (II) fractures involving the coronal portion of the tooth with cohesive failure of the composite resin; (III) oblique tooth and restoration fracture with periodontal involvement; and (IV) vertical root and coronal fracture. Varying crosshead speeds of 0.5-5.0 mm/min did not influence the failure load of restored maxillary premolars; however, increasing the crosshead speed to 10 mm/min decreased the failure load values and the degree of tooth structural damage.

Influence of crosshead speed on failure load and failure mode of restored maxillary premolars

We analyzed the effect of the crosshead speed of an applied load on failure load and failure mode of restored human premolars. Fifty intact, noncarious human premolars were selected. Class II mesio-occlusodistal preparations were made with a water-cooled high-speed preparation machine, and the teeth were restored with composite resin. The specimens were divided into five groups (n = 10 each) and tested individually in a mechanical testing machine, in which a 6.0-mm-diameter steel cylinder was mounted to vary the crosshead speed: v0.5: 0.5 mm/min; v1: 1.0 mm/min; v2.5: 2.5 mm/min; v5: 5.0 mm/min; and v10: 10.0 mm/min. The cylinder contacted the facial and lingual ridges beyond the margins of the restorations. Peak load to fracture was measured for each specimen (N). The means were calculated and analyzed with one-way analysis of variance followed by Tukey's test (a = 0.05). The mean load at failure values were (N) as follows: v0.5, 769.4 ± 174.8; v1, 645.2 ± 115.7; v5, 614.3 ± 126.0; v2.5, 609.2 ± 208.1; and v10, 432.5 ± 136.9. The fracture modes were recorded on the basis of the degree of the tooth structural and restorative damage: (I) fracture of the restoration involving a small portion of the tooth; (II) fractures involving the coronal portion of the tooth with cohesive failure of the composite resin; (III) oblique tooth and restoration fracture with periodontal involvement; and (IV) vertical root and coronal fracture. Varying crosshead speeds of 0.5–5.0 mm/min did not influence the failure load of restored maxillary premolars; however, increasing the crosshead speed to 10 mm/min decreased the failure load values and the degree of tooth structural damage.

The influence of polymerization type and reinforcement method on flexural strength of acrylic resin.

The aim of this study was to evaluate the flexural strength of acrylic resin bars by varying the types of resin polymerization and reinforcement methods. Fourteen groups (N=10) were created by the interaction of factors in study: type of resin (self-cured (SC) or heat-cured (HC)) and reinforcement method (industrialized glass fiber (Ind), unidirectional glass fiber (Uni), short glass fiber (Short), unidirectional and short glass fiber (Uni-Short), thermoplastic resin fiber (Tpl), and steel wire (SW)). Reinforced bars (25×2×2 mm) were tested in flexural strength (0.5 mm/min) and examined by scanning electron microscopy (SEM). Data (MPa) were submitted to factorial analysis, ANOVA, and Tukey and T-student tests (a=5%) showing significant interaction (P=0.008), for SC: Uni (241.71±67.77)a, Uni-Short (221.05±71.97)a, Ind (215.21±46.59)ab, SW (190.51±31.49)abc, Short (156.31±28.76)bcd, Tpl (132.51±20.21)cd, Control SC (101.47±19.79)d and for HC: Ind (268.93±105.65)a, Uni (215.14±67.60)ab, Short (198.44±95.27)abc, Uni-Short (189.56±92.27)abc, Tpl (161.32±62.51)cd, SW (106.69±28.70)cd, and Control HC (93.39±39.61)d. SEM analysis showed better fiber-resin interaction for HC. Nonimpregnated fibers, irrespective of their length, tend to improve fracture strength of acrylics.

Retrieval technique for full-arch implant-supported fixed prosthesis: a clinical report.

In the event of the loss of an implant and to take advantage of the preexisting structures, a rescue procedure that allows continuous use of the original fixed restoration during the restoration of the tripod support at the implant level can be used. When nonphysiological occlusion forces are avoided, the success rate of this rescue procedure is very similar to any other rehabilitation made following a conventional protocol. Furthermore, the fact that the patient has already adapted to the prosthesis position and its vertical dimension results in easier functional adaptation in the postoperative period and, consequently, greater comfort.

Effect of glass fiber incorporation on flexural properties of experimental composites.

This study evaluated the effect of fiber addiction in flexural properties of 30 wt% silica filled BisGMA resin (FR) or unfilled Bis-GMA (UR). Ten groups were created (N = 10) varying the resin (FR or UR) and quantity of glass fibers (wt%: 0, 10, 15, 20, and 30). Samples (10 × 2 × 1 mm) were submitted to flexural strength test following SEM examination. Data were analyzed by two-way ANOVA, Tukey, and Student t-test (α = 0.05). Results for flexural strength (MPa) were FR-groups: 0% (442.7 ± 140.6)(C), 10% (772.8 ± 446.3)(ABC), 15% (854.7 ± 297.3)(AB), 20% (863.4 ± 418.0)(A), 30% (459.5 ± 140.5)(BC); UR-groups: 0% (187.7 ± 120.3)(B), 10% (795.4 ± 688.1)(B), 15% (1999.9 ± 1258.6)(A), 20% (1911.5 ± 596.8)(A), and 30% (2090.6 ± 656.7)(A), and for flexural modulus (GPa) FR-groups: 0% (2065.63 ± 882.15)(B), 10% (4479.06 ± 3019.82)(AB), 15% (5694.89 ± 2790.3)(A), 20% (6042.11 ± 3392.13)(A), and 30% (2495.67 ± 1345.86)(B); UR-groups: 0% (1090.08 ± 708.81)(C), 10% (7032.13 ± 7864.53)(BC), 15% (19331.57 ± 16759.12)(AB), 20% (15726.03 ± 8035.09)(AB), and 30% (29364.37 ± 13928.96)(A). Fiber addiction in BisGMA resin increases flexural properties, and the interaction between resin and fibers seems better in the absence of inorganic fillers increasing flexural properties.

Biocompatibility of three bioabsorbable membranes assessed in FGH fibroblasts and human osteoblast like cells culture.

OBJECTIVES: Specific physical and chemical features of the membranes may influence the healing of periodontal tissues after guided tissue regeneration (GTR). The aim of the present investigation was to analyze the biological effects of three bioabsorbable membranes. The hypothesis is that all tested membranes present similar biological effects. METHODS: Human osteoblast like-cells (SaOs-2) and gingival fibroblasts FGH (BCRJ -RJ) were cultured in DMEM medium. The viability of the cells cultured on the membranes was assesses using 3-(4,5-Dimethylthiazol-2-yl)-2,5-diphenyltetrazolium bromide (MTT). Quantitative determination of activated human Transforming Growth Factor beta 1 (TGF-ß1) on the supernatants of the cell culture was observed. Samples were examined using scanning electron microscope (SEM). RESULTS: SaOs2, in 24 hours, PLA group showed higher values when compared to other groups (P < 0.05). All groups presented statistical significance values when compared two times. In 4 h and 24 h, for the fibroblasts group, significantly difference was found to PLA membrane, when compared with the other groups (p < 0.05). For TGFß1 analyzes, comparing 4 and 24 h, for the osteoblast supernatant, COL1 and PLA groups showed statistically significant difference (p <0,008). On the analysis of culture supernatants of fibroblasts, in 24 hours, only PLA group presented significant difference (p = 0,008). CONCLUSIONS: The biomaterials analyzed did not show cytotoxicity, since no membrane presented lower results than the control group. PLA membrane presented the best performance due to its higher cell viability and absorbance levels of proliferation. Both collagen membranes showed similar results either when compared to each other or to the control group.

Influence of abutment screw design and surface coating on the bending flexural strength of the implant set.

The purpose of this study was to analyze the influence of the setting and the presence of solid lubricant on the abutment screw surface on the flexural strength of the joint implant/abutment/screw. Forty abutments were connected to external hex implants, divided into 4 groups (n = 10): FE (titanium alloy screw threaded in the extremity), LE (titanium alloy screw with solid lubricant and thread in the extremity), FT (titanium alloy screw with threaded in all its length), and LT (titanium alloy screw with solid lubricant and thread in all its length). Through the mechanical flexural test, the implant/abutment resistance was evaluated with load applied perpendicular to the long axis in a mechanical testing machine (EMIC) under a speed of 0.5 mm/min. Data were submitted to a statistics test, and results showed statistically significant differences between the FE group and the other groups, and the FE group showed the lowest values. The LE group showed greater values than the LT group, and the values were statistically significant. According to the methodology used, it can be concluded that within noncoated titanium screws, a screw threaded along its entire length provided greater rigidity to the implant set, while with the screw containing solid lubricant, the screw threaded in all its length provided less rigidity of the implant set than screws with the thread only on the end. Among screws with the same geometry, those with the solid lubricant are statistically higher than those which do not have threads just at the end, but those with threads along their entire length do not show statistically significant differences.

Influence of chlorhexidine on dentin adhesive interface micromorphology and nanoleakage expression of resin cements.

This study focused on adhesive interface morphologic characterization and nanoleakage expression of resin cements bonded to human dentin pretreated with 1% chlorhexidine (CHX). Thirty-two non-carious human third molars were ground flat to expose superficial dentin. Resin composite blocks were luted to the exposed dentin using one conventional (RelyX ARC) and one self-adhesive resin cement (RelyX U100), with/without CHX pretreatment. Four groups (n = 8) were obtained: control groups (ARC and U100); experimental groups (ARC/CHX and U100/CHX) were pretreated with 1% CHX prior to the luting process. After storage in water for 24 h, the bonded teeth were sectioned into 0.9 × 0.9 mm(2) sticks producing a minimum of 12 sticks per tooth. Four sticks from each tooth were prepared for hybrid layer evaluation by scanning electron microscope analysis. The remaining sticks were immersed in silver nitrate for 24 h for either nanoleakage evaluation along the bonded interfaces or after rupture. Nanoleakage samples were carbon coated and examined using backscattered electron mode. Well-established hybrid layers were observed in the groups luted with RelyX ARC. Nanoleakage evaluation revealed increase nanoleakage in groups treated with CHX for both resin cements. Group U100/CHX exhibited the most pronouncing nanoleakage expression along with porous zones adjacent to the CHX pretreated dentin. The results suggest a possible incompatibility between CHX and RelyX U100 that raises the concern that the use of CHX with self-adhesive cements may adversely affect resin-dentin bond.

Effect of various aging protocols and intermediate agents on the bond strength of repaired composites.

PURPOSE: To evaluate the effect of two adhesive systems and different aging protocols on the bond strength of a -repaired microhybrid composite. MATERIALS AND METHODS: Eighty test specimens (n = 20) and 10 control specimens measuring 8 x 4 mm were fabricated of a microhybrid composite (4 Seasons, shade A2) and grouped according to time/aging protocol: G1: 24 h in artificial saliva; G2: 7 days in artificial saliva; G3: 30 days in artificial saliva; G4: artificial accelerated aging (AAA) for 384 h; G5: control. After aging, samples were submitted to three types of surface treatment: SB2: Adper Single Bond 2, a two-step adhesive (3M ESPE); SB3: Adper Scotchbond Multi-Purpose, a three-step adhesive (3M ESPE); C: without application of adhesive (control). After this, test specimens were repaired with the same composite of a different shade (C3), and submitted to the microtensile test at a crosshead speed of 0.5 mm/min. Failure modes were analyzed by scanning electron microscopy (Jeol JSM 7500). Statistical analysis was performed using ANOVA and Tukey's test (p < 0.05). RESULTS: G2/SB2 presented significantly lower bond strength values in comparison with the other groups (p < 0.05). The control group presented the highest bond strength values, which differed statistically significantly from SB3, G3/SB2, and G4/SB2 (p < 0.05). Fractographic analysis demonstrated that most samples presented predominantly cohesive failures, excepting GI/SB2, which presented mixed and cohesive failures, and G4/SB2 and G1/SB3, which showed adhesive failures. CONCLUSION: The repair was more effective when performed after a short period of time and when the 3-step adhesive system (SB3) was used.

Mechanical properties of cast commercially pure titanium simulating ceramic firing cycles.

AIM: To evaluate the mechanical properties (ultimate tensile strength, elongation and hardness) of the commercially pure titanium (cp Ti) as casting and after ceramic firing cycles. MATERIALS AND METHODS: Dumbbell-shaped specimens were prepared for the tensile strength testing. Disk-shaped cast specimens were used for microhardness testing. The ceramic firing cycles were made simulating a low fusion ceramic application. Tensile testing was conducted in a universal testing machine at a crosshead speed of 1 mm/min until failure. Ultimate tensile strength and elongation were recorded. The fracture mode was analyzed by scanning electron microscopy. Vickers hardness was measured in a hardness tester. The data from the tensile and hardness tests were subjected to a one-way analysis of variance and Tukey's test (α = 0.05). RESULTS: The mean values of tensile strength were not changed by the ceramic firing cycles. Lower hardness was observed for cp Ti as casting compared with Ti cast after the firing cycles. CLINICAL SIGNIFICANCE: The ceramic firing cycles did not show any considerable prejudicial effects on the mechanical properties of the cp Ti.

Retrieval technique for the Branemark Novum protocol: replacement of a lost implant.

In the past, the Branemark Novum protocol for the immediate functional loading of a mandibular fixed implant supported prosthesis provided an effective alternative for select patients. However, the manufacturer has discontinued this design, and only a few selected prosthetic-related replacement components are currently available. This clinical report presents the loss of an implant associated with a discontinued system. To take advantage of all of the preexisting components, it proposes a rescue procedure that allows continuous use of the original fixed restoration during the restoration of the tripod support at the implant level.

Short-term PTH administration increases dentine apposition and microhardness in mice.

OBJECTIVE: The purpose of this study is to investigate the effects of intermittent parathyroid hormone (PTH) administration on the apposition rate and structural features of dentine from mouse incisors. METHODS: Young male A/J Unib mice were treated daily for 6 and 10 days with 40 µg/kg of hPTH 1-34 or a vehicle. Dentine apposition rates measured by fluorescent labels (tetracycline and calcein) and alkaline phosphatase (ALP) plasma levels were evaluated after 6 days of treatment. Knoop microhardness testing and element content measurements in at.% of calcium (Ca), phosphorus (P), oxygen (O), and magnesium (Mg) in the peritubular and intertubular dentine were performed by Energy Dispersive X-ray (EDX) microanalysis via Scanning Electron Microscopy (SEM) after 10 days of treatment. RESULTS: Histometric analysis revealed an increase of 5% in the apposition rate of dentine and 25% in the ALP plasma levels in the PTH treated group. In addition, knoop microhardness testing revealed that the animals treated with PTH had a greater microhardness (11%). EDX microanalysis showed that PTH treatment led to increases in P (23%) and Ca (53%) at.% content, as well as the Ca/P ratio (24%) in peritubular dentine. The chemical composition of intertubular dentine did not vary between the groups. CONCLUSIONS: These findings indicate that intermittent administration of hPTH (1-34) increases apposition and mineralization of the dentine during young mice incisor formation.